Description
Jiangsu Liangyi is professional manufacturer of 1.4878,X8CrNiTi18-10,X8CrNiTi1810,X8CrNiTi18.10 open die forging parts and seamless rolled steel forged rings from china
Following is the shape of 1.4878,X8CrNiTi18-10,X8CrNiTi1810,X8CrNiTi18.10 forging steel material that we could do is:X8CrNiTi18-10 Forged Steel round bars square bars Flat bars Rectangles Bars Rods,X8CrNiTi18.10 Forged forging steel rings seamless rolled rings,1.4878 Forged Forging Steel Hubs housing shell Sleeves Bushes Bushing Cases Hollow Bars,1.4878 Forged Forging Steel Discs Disks Blocks plates,X8CrNiTi18-10 Forged Forging Steel Pipe Tubes Tubings Piping Shells Casings Case barrels Housings.
Following is forging products of 1.4878,X8CrNiTi18-10,X8CrNiTi1810,X8CrNiTi18.10 material that is used in following industry
X8CrNiTi18-10 Forged Forging Valve Balls,valve Bonnets,valve Body Bodies ,valve Stems,valve closures, valve seat rings, valve core, valve discs,for H type two way 2‐way one way back pressure valves, ball valve,check valve,gate valve
X8CrNiTi18.10 Forged Forging Steel Butterfly Valve Main Shafts Spindles
1.4878 Forged Forging Swept branches outlets steel fittings swept saddles
X8CrNiTi18-10 Forged Forging downhole drilling tool Mud Motor Splined Drive shafts,Down hole Electric electrical submersible pumps ESP motor Splined Shaft
X8CrNiTi18.10 Forged Forging Steels Christmas Trees wellhead Spool Body Bodies cylinder
1.4878 Forged Forging venturi cone meter Body Bodies Blocks
1.4878 Forged Forging Steel gate valves Body Bodies bespoke flat bars
X8CrNiTi18-10 forged steel Flowseal cryogenic High Performance BV Butterfly Valves HPBV shaft
X8CrNiTi18-10 forging steel Oil measurement valve Spool Ultrasonic flow meter bodies Body
X8CrNiTi18.10 Forged Forging Steel double studded adapter flange
X8CrNiTi18.10 Forged Forging Steel integral Mud Flange Flanged outlet Studded crosses
1.4878 Forged Forging Steel Casing Heads,Tubing Heads,Casing Hangers,Tubing Hangers,Tubing Spools,Casing Spools,Spacer Spools
X8CrNiTi18.10 Forged Forgig Steel nuclear reactor coolant pump Casing Shells body bodis blocks,nuclear reactor coolant pumps containment seal chamber Rooms,nuclear reactor coolant pumps containment seal chamber Rooms
X8CrNiTi18.10 Forged Forging turbomachinery turbo centrifugal compressor Impeller,Compressor Shrouded Impellers
X8CrNiTi18.10 Forged Forging Steel Forged Single Double Bossed boss Blanks FLANGED BOSSES
X8CrNiTi18.10 Forged Forging Steel PUMP Casing cover.PUMP BARREL,pump impeller,pump shafts, pump housing, pump shells,pump body,pump wear rings,pump case casing.
1.4878 Forged Forging forge Steel transition Cone
1.4878 Forged Forging Steel Pressure Vessel Reactor Nozzles
X8CrNiTi18-10 forged forging steel pipes tubes shells piping tubing barrels housing, tube sheets,baffle plates, nozzles, channel flanges for boiler, heat exchanger,pressure vessel,reactors, heaters
1.4878 Exhibits good corrosion resistance in natural environmental media (water rural and industrial atmospheres).The prerequisite is that chlorine and salt concentrations and concentration of nitric or organic acids are low.Automotive industry, construction industry, chemical industry, food industry, aerospace, mechanical engineering.
FOllowing is production standard of 1.4878 forged material
EN 10095: 1999 Heat Resisting Steels and Nickel Alloys
EN 10297-2: 2005 Seamless circular steel tubes for mechanical and general engineering purposes. Stainless steel. Technical delivery conditions
EN 10088-1: 2005 Stainless steels. List of stainless steels
FOllowing is chemical compostion of X8CrNiTi18.10 forged steel rings
C max 0.1
Si max 1
Mn max 2
Ni 9 - 12
P max 0.045
S max 0.015
Cr 17 - 19
Ti max 0.8
Following of X8CrNiTi18-10 forging parts heat treatment mechanical property Delivery condition :
Rm - Tensile strength (MPa) (+AT) 500-720
Rp0.2 0.2% proof strength (MPa) (+AT) 190
A - Min. elongation at fracture (%) (+AT) 40
Brinell hardness (HB): (+AT) 215
Tensile test specimens shall betaken from the test location shown on the Purchasers X8CrNiTi18-10 forged parts drawing.The long dimension of the specimens should approximate the tangential direction of the disc forging.
Four tensile specimens (two RT tensiles and two 650°C tensiles)shall be tested from the test location of each disc.The two RT tensile tests shall be 180 degrees apart and the 650°C tensile tests shall be 180 degrees apart and 90 degrees from the RT tensile test positions.
The tensile specimens shall be the Standard Round 0.500-inch (12.5 mm)diameter with 2 inch (50 mm) gage length according to ASTM A370.Yield strength shall be determined at 0.2% offset.
Brinell hardness is to be determined at 10 locations:4 on each rim face 90 degrees from each other and one at the center (or near the bore area)of each face.
Brinell hardness shall be also determined on each tension and creep rupture test specimen.
All our finish production of 1.4878,X8CrNiTi18-10 forged steel material should will done in Following NDE shall be performed in delivery condition:
- Visual inspection
Material verification test
- 100% UT- inspection according to EN 10228-3 (table 3). Depending on the forging geometry,
following inspection types are applicable:
- for 1.4542 forging bar shape components; type 1 (inspection may also be carried out as per EN10308 for type 1)
- for X5CrNiCuNb16-4 forged discs and plate- like components: type 2
- for X5CrNiCuNb164 forging ring or bushing- like components: type 3b and 3
Welcome your inquiry of 1.4878,X8CrNiTi18-10,X8CrNiTi1810,X8CrNiTi18.10 forging forged steel parts