Description
Jiangsu Liangyi professional manufacturer of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021 open die forging parts and seamless rolled steel forged rings from china
Following is the shape of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging steel material that we could do is:Nimonic 105 Forged Steel round bars square bars Flat bars Rectangles Bars Rods,Nimonic ALloy 105 Forged forging steel rings seamless rolled rings,Nimonic 105 Forged Forging Steel Hubs housing shell Sleeves Bushes Bushing Cases Hollow Bars,UNS N13021 Forged Forging Steel Discs Disks Blocks plates,ALloy 105 Forged Forging Steel Pipe Tubes Tubings Piping Shells Casings Case barrels Housings.
Following is forging products of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 material that is used in following industry
Nimonic ALloy 105 Forged Forging Gas Compressor Turbine Blades steel Flat Rectangles Bars
Nimonic 105 Forged Forging Gas steam turbine disks, turbine impeller,turbine blisk,turbine discs
ALloy 105 Forging Steel Forging Forged Gas Steam Turbine Doubled-headed Double end Studs Fasteners Bolts bolting
UNS N13021 Forging Steel gas steam Turbine Guide Rings,seal rings Labyrinth Rings Packing Seal Diaphragm & Seal Ring Rotor End Rings contours Casing Rings
ALloy 105 Forged Forging Steel Gas Steam turbine diaphragm diapharagm nozzles
Nimonic 105 Forged Forging Gas Turbine LPT 1st & 2st 2nd Stg Stage Turbine Case Casings
Nimonic 105 Forged Forging Steel power plant steam turbine control reheat valve disc Disk
ALloy 105 Forged forging Gas Steam Turbine Valve Spindles/Stems/Rods,
ALloy 105 Forging Steel Gas Steam Turbine MSV/GV/CV/CRV Valve Seats, Valve Cores, Valve Sleeves Spools,,Main Steam Valve Covers Bonnets Sleeves
NIMONIC Alloy 105 a wrought nickel-colbalt-chromium base alloy which also contains molybdenum, aluminium and titanium which results in a high strength alloy that can be used in conditions up to 950°C with good creep resistance. Alloy 105 is used for turbine blades, discs, forgings, ring sections, bolts and fasteners.
The raw material OF Nimonic ALloy 105 FORGING Parta can be manufactured according to one of these three methods:
Method A: Air melt and vacuum refined (AM/VR),
Method B: Vacuum induction melted and vacuum arc refined (VIM/VAR).
Method C: Air melt and vacuum arc refined (AM/VAR).
Chemical composition of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging turbine parts is as
The chemical composition of NIMONIC 105 is as follows:
Aluminum:4.5 - 4.9
Boron:0.003 - 0.01
Carbon:0.12 max
Chromium:14 - 15.7
Cobalt:18 - 22
Copper:0.2 max
Iron:1 max
Manganese:1 max
Molybdenum:4.5 - 5.5
Nickel:Balance
Silicon:1 max
Sulphur:0.01 max
Titanium:0.9 - 1.5
Zirconium:0.15 max
HEAT TREATMENT Nimonic 105 forged turbine blade material is as followin
SOLUTION TREATMENT (Stage1)
Temperature:1150 "C
Time:4 hr
Cooling Rate:Air Cooling
FIRST PRECIPITATION TREATMENT (Stage2)
Temperature:1030 'C
Time:16 hr
Cooling Rate:Air Cooling
SECOND PRECIPITATION TREATMENT
Temperature:700 "C
Time:min 16 hours
Cooling Rate:Air Cooling
mechanical property of for Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forged round bars is as follow
Tensile strength (precipitation hardened, value at room temperature) 1150 MPa 167000 psi
Yield strength (precipitation hardened, value at room temperature, @strain 0.200%) 770 MPa 112000 psi
Elongation at break (precipitation hardened) 25% 25%
The material of Nimonic ALloy 105 forged parts shall be free from blisters, cracks and slag inclusion. The surface ofmaterial shall be even and free from mill scale, forging folds, corrosion damage orother faults which may affect their usability.
Ultrasonic examination shall be carried out on Nimonic ALloy 105 each bar, Nimonic ALloy 105 forging or Nimonic ALloy 105 finished parts.Unacceptable defects are:
Cracks
Fault indications corresponding to a flat-bottomed hole FBH> ф3mm
Fault indications corresponding to a flat-bottomed hole FBH2 ф1.5mm with alength 2 30mm
Reports shall be submitted in the event of:
Fault indications corresponding to a flat-bottomed hole FBH 2 ф2mm
Fault indications corresponding to a flat-bottomed hole FBH 2 ф1 .5mm withmeasurable length.
SELECTION OF TEST SAMPELS of Nimonic ALloy 105 forged material
From each cast, six test samples of sufficient length shall be taken randomly throughout the cast but representative of six different extrusions of the samenominal dimensions.
PERPARATION OF TEST SAMPELS of Nimonic ALloy 105 forged products
Nominal Dimensions of Bar 10 mm to less than 20 mm
(a) The test samples shall be fully heat treated in accordance with the requirementsof this specification.
(b) Two* test pieces shall be machined coaxially from each test samples.
One test piece from each test sample shall be subjected to the stress rupture test at 815 degree, the remaining test piece to be subjected to the stress rupture atdegree.
. Nominal Dimensions of Bar 20 mm up to and including 50 mm
(a) The test samples shall be single-blow or multi-blow in one heat, side forged at atemperature of 1140+-10degree to a Cheese" having the. following nominalthickness.
Nominal Dimensions of Bar (mm):20<=40, Nominal Dimensions of "Cheese" (mm):13
Nominal Dimensions of Bar (mm):>40<=50, Nominal Dimensions of "Cheese" (mm):20
Nominal Dimensions of "Cheese" (mm)
(b) Tow* test bars shall be taken from each Cheese". The positions from which thetest pieces shall be taken are indication in Appendix2 of this specification.
* One test piece from each "Cheese" shall be subjected to the stress rupture at 815DEGREE, the remaining test piece to be subjected to the stress rupture at 950 DEGREE
(c) The test bars" shall be finally heat treated in accordance with the requirement
Welcome your inquiry of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging parts
Following is the shape of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging steel material that we could do is:Nimonic 105 Forged Steel round bars square bars Flat bars Rectangles Bars Rods,Nimonic ALloy 105 Forged forging steel rings seamless rolled rings,Nimonic 105 Forged Forging Steel Hubs housing shell Sleeves Bushes Bushing Cases Hollow Bars,UNS N13021 Forged Forging Steel Discs Disks Blocks plates,ALloy 105 Forged Forging Steel Pipe Tubes Tubings Piping Shells Casings Case barrels Housings.
Following is forging products of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 material that is used in following industry
Nimonic ALloy 105 Forged Forging Gas Compressor Turbine Blades steel Flat Rectangles Bars
Nimonic 105 Forged Forging Gas steam turbine disks, turbine impeller,turbine blisk,turbine discs
ALloy 105 Forging Steel Forging Forged Gas Steam Turbine Doubled-headed Double end Studs Fasteners Bolts bolting
UNS N13021 Forging Steel gas steam Turbine Guide Rings,seal rings Labyrinth Rings Packing Seal Diaphragm & Seal Ring Rotor End Rings contours Casing Rings
ALloy 105 Forged Forging Steel Gas Steam turbine diaphragm diapharagm nozzles
Nimonic 105 Forged Forging Gas Turbine LPT 1st & 2st 2nd Stg Stage Turbine Case Casings
Nimonic 105 Forged Forging Steel power plant steam turbine control reheat valve disc Disk
ALloy 105 Forged forging Gas Steam Turbine Valve Spindles/Stems/Rods,
ALloy 105 Forging Steel Gas Steam Turbine MSV/GV/CV/CRV Valve Seats, Valve Cores, Valve Sleeves Spools,,Main Steam Valve Covers Bonnets Sleeves
NIMONIC Alloy 105 a wrought nickel-colbalt-chromium base alloy which also contains molybdenum, aluminium and titanium which results in a high strength alloy that can be used in conditions up to 950°C with good creep resistance. Alloy 105 is used for turbine blades, discs, forgings, ring sections, bolts and fasteners.
The raw material OF Nimonic ALloy 105 FORGING Parta can be manufactured according to one of these three methods:
Method A: Air melt and vacuum refined (AM/VR),
Method B: Vacuum induction melted and vacuum arc refined (VIM/VAR).
Method C: Air melt and vacuum arc refined (AM/VAR).
Chemical composition of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging turbine parts is as
The chemical composition of NIMONIC 105 is as follows:
Aluminum:4.5 - 4.9
Boron:0.003 - 0.01
Carbon:0.12 max
Chromium:14 - 15.7
Cobalt:18 - 22
Copper:0.2 max
Iron:1 max
Manganese:1 max
Molybdenum:4.5 - 5.5
Nickel:Balance
Silicon:1 max
Sulphur:0.01 max
Titanium:0.9 - 1.5
Zirconium:0.15 max
HEAT TREATMENT Nimonic 105 forged turbine blade material is as followin
SOLUTION TREATMENT (Stage1)
Temperature:1150 "C
Time:4 hr
Cooling Rate:Air Cooling
FIRST PRECIPITATION TREATMENT (Stage2)
Temperature:1030 'C
Time:16 hr
Cooling Rate:Air Cooling
SECOND PRECIPITATION TREATMENT
Temperature:700 "C
Time:min 16 hours
Cooling Rate:Air Cooling
mechanical property of for Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forged round bars is as follow
Tensile strength (precipitation hardened, value at room temperature) 1150 MPa 167000 psi
Yield strength (precipitation hardened, value at room temperature, @strain 0.200%) 770 MPa 112000 psi
Elongation at break (precipitation hardened) 25% 25%
The material of Nimonic ALloy 105 forged parts shall be free from blisters, cracks and slag inclusion. The surface ofmaterial shall be even and free from mill scale, forging folds, corrosion damage orother faults which may affect their usability.
Ultrasonic examination shall be carried out on Nimonic ALloy 105 each bar, Nimonic ALloy 105 forging or Nimonic ALloy 105 finished parts.Unacceptable defects are:
Cracks
Fault indications corresponding to a flat-bottomed hole FBH> ф3mm
Fault indications corresponding to a flat-bottomed hole FBH2 ф1.5mm with alength 2 30mm
Reports shall be submitted in the event of:
Fault indications corresponding to a flat-bottomed hole FBH 2 ф2mm
Fault indications corresponding to a flat-bottomed hole FBH 2 ф1 .5mm withmeasurable length.
SELECTION OF TEST SAMPELS of Nimonic ALloy 105 forged material
From each cast, six test samples of sufficient length shall be taken randomly throughout the cast but representative of six different extrusions of the samenominal dimensions.
PERPARATION OF TEST SAMPELS of Nimonic ALloy 105 forged products
Nominal Dimensions of Bar 10 mm to less than 20 mm
(a) The test samples shall be fully heat treated in accordance with the requirementsof this specification.
(b) Two* test pieces shall be machined coaxially from each test samples.
One test piece from each test sample shall be subjected to the stress rupture test at 815 degree, the remaining test piece to be subjected to the stress rupture atdegree.
. Nominal Dimensions of Bar 20 mm up to and including 50 mm
(a) The test samples shall be single-blow or multi-blow in one heat, side forged at atemperature of 1140+-10degree to a Cheese" having the. following nominalthickness.
Nominal Dimensions of Bar (mm):20<=40, Nominal Dimensions of "Cheese" (mm):13
Nominal Dimensions of Bar (mm):>40<=50, Nominal Dimensions of "Cheese" (mm):20
Nominal Dimensions of "Cheese" (mm)
(b) Tow* test bars shall be taken from each Cheese". The positions from which thetest pieces shall be taken are indication in Appendix2 of this specification.
* One test piece from each "Cheese" shall be subjected to the stress rupture at 815DEGREE, the remaining test piece to be subjected to the stress rupture at 950 DEGREE
(c) The test bars" shall be finally heat treated in accordance with the requirement
Welcome your inquiry of Nimonic ALloy 105, Nimonic 105, ALloy 105,UNS N13021,nimonic105 forging parts